PVC resin
| PRAECIPUUS | Sg3 | Sg5 | TY DCCC | Sg8 | DG-DCC | DG-1000s | |
| Viscosity, ml / g | 135-127 | 118-107 | 94-86 | 86-73 | - | - | |
| K valorem | 72-71 | 68-66 | 62-60 | 59-55 | - | - | |
| Mediocris gradu polymerization | 1370-1251 | 1135-981 | 850-750 | 740-650 | 651-750 | 981-11080 | |
| Maecenas particularum, pieces ≤ | 16 | 16 | 20 | 20 | 30 | 30 | |
| Volatile contentus (includinghumorem)%≤ | 0,3 | 0,4 | 0,3 | 0,4 | 0,3 | 0,3 | |
| Apparent density g / ml ≥ | 0.45 | 0.48 | 0,52 | 0,52 | 0.53-0.61 | 0.51-0.57 | |
| Residuo post cribrum% | 0.35mm, cribrum pore | - | - | - | - | 0.1 | 0.1 |
| 0.25mm, cribrum pore | 1.6 | 1.6 | 1.2 | 1.6 | - | - | |
| 0.063mm, cribroporo | 97 | 97 | 97 | 97 | - | - | |
| Numerus frumenti / 400cm2≤ | 20 | 20 | 30 | 30 | 30 | 20 | |
| Plasticizer effusio capacitatem,Value of 100g resinTago | 26 | 19 | 12 | 12 | 12 | 20 | |
| CandorDegree (CLX ℃, 10min),% ≥ | 78 | 78 | 78 | 75 | 90 | 90 | |
| Conductivity AqueumextractuS / (cm.g)≤ | 5 | - | - | - | - | - | |
| VCM RELICTUM, μG / G≤ | 1 | 1 | 1 | 1 | 1 | 1 | |